A Systematic Review and Network Meta-Analysis of Biomedical Mg Alloy and Surface Coatings in Orthopedic Application

Lu, XinYue; Cai, HongXin; Li, Yu Ru; Zheng, Xinru; Yun, Jiahao; Li, Wenhui; Geng, XiaoYu; Kwon, Jae-Sung; Jiang, Heng Bo

doi:https://doi.org/10.1155/2022/4529520

Bioinorganic Chemistry and Applications

On this page

Abstract Introduction Materials and Methods Results Discussion Conclusions Data Availability Conflicts of Interest Authors’ Contributions Supplementary Materials References Copyright Related Articles

Special Issue

Development, Improvement, and Applications of Biomedical Magnesium

View this Special Issue

Review Article | Open Access

Volume 2022 | Article ID 4529520 | https://doi.org/10.1155/2022/4529520

A Systematic Review and Network Meta-Analysis of Biomedical Mg Alloy and Surface Coatings in Orthopedic Application

XinYue Lu,¹HongXin Cai,²Yu Ru Li,¹Xinru Zheng,¹Jiahao Yun,¹Wenhui Li,¹XiaoYu Geng,¹Jae-Sung Kwon,²and Heng Bo Jiang¹

Academic Editor: Giuseppe Ciccarella

Received17 Jan 2022

Accepted19 Feb 2022

Published31 Mar 2022

Abstract

Magnesium alloys have great application prospects as ideal bone implant materials. However, their poor corrosion resistance limits their clinical orthopedic application. Surface modification promotes the corrosion resistance of magnesium. Conversion coatings, such as calcium phosphate (Ca-P) coating, microarc oxidation (MAO) treatment, and fluoride (FLU) treatment, have been extensively investigated in in vivo studies. This systematic review and network meta-analysis compared the influence of different conversion coatings on bone repair, material properties, and systemic host response in orthopedic applications. Using the PICOS model, the inclusion criteria for biodegradable magnesium and its alloys were determined for in vivo studies. Four databases were used. The standard and weight mean differences with 95% confidence intervals were used to analyze new bone formation and degradation rate. Network structure and forest plots were created, and ranking probabilities were estimated. The risk of bias and quality of evidence were assessed using SYRCLE, CERQual, and GRADE tools. In the qualitative analysis, 43 studies were selected, and the evaluation of each outcome indicator was not entirely consistent from article to article. In the quantitative analysis, 21 articles were subjected to network meta-analysis, with 16 articles on implant degradation and 8 articles for new bone formation. Additionally, SUCRA indicated that Ca-P coating exhibited the highest corrosion resistance, followed by FLU treatment. MAO demonstrated the best capability for new bone formation, followed by Ca-P coating. Ca-P coating exhibited the highest overall performance. To conclude, coated Mg can promote better new bone formation than bare Mg and has considerable biocompatibility. Ca-P-coated Mg and MAO-coated Mg have the greatest potential to significantly promote corrosion resistance and bone regeneration, respectively. The findings of this study will provide a theoretical basis for the investigation of composite coatings and guidance for the orthopedic application of Mg bone implants.

1. Introduction

Magnesium alloys are biodegradable metallic bone graft materials with mechanical properties (e.g., density, elastic modulus, yield strength, and compressive strength) similar to those of natural human bones [1, 2]. Multiple studies have demonstrated that Mg alloys have excellent biocompatibility, osteoconductivity, osteoinductivity, antibacterial, anti-inflammatory, and other biological properties [3]. Owing to these excellent characteristics, Mg alloys have a wide range of application prospects in orthopedic applications and can be used for bone fracture, bone defect healing, and guided bone regeneration [2]. An Mg alloy can be safely degraded in vivo over time, after support and protection. Without the need for second operation [4, 5], it can reduce the suffering of patients, particularly the elderly who are prone to osteoporosis and children. Owing to the decrease in metal particles and the stay of ions, Mg alloys cause less toxic side effects [6–8], which reduce the risks of the stress shielding effect [9] as well as the possibility of a second fracture after surgeries [10, 11]. Furthermore, Mg alloys have considerable potential as internal fixation materials for fracture [12]. In addition, the Mg ions produced after degradation are common in vivo metabolites, which are stored in the bones; therefore, within the normal range [13], magnesium ions are not toxic to the human body.

Despite various advantages, poor corrosion resistance limits the extensive application of Mg alloys. Therefore, current research on magnesium has focused on improving their corrosion resistance. There are two main ways to improve corrosion resistance, i.e., alloying [14] and coating [15].

Alloying can optimize the composition and performance of Mg alloys and is an effective but costly strategy [16–18]. It may also cause deterioration under certain specific conditions. Compared to alloying, coating is an economical and effective strategy. Surface modification forms a corrosion-resistant film on the surface of the Mg alloy substrate and prevents the external medium from corroding the Mg alloy, which results in improved corrosion resistance [18]. To date, various coatings have been developed, and surface modifications can be divided into two types according to the formation mechanism: conversion coatings and deposition coatings [19].

Conversion coating is an in situ coating formed by the chemical reaction between the Mg alloy substrate and the solution, which involves the complex interaction of metal dissolution and precipitation. Chemical or electronic coating techniques involving salts and oxides result in a strong adhesion between the magnesium substrate and coatings, which reduces the risk of the surface coatings peeling off [20, 21].

Multiple clinical studies have confirmed that animal experiments are essential to evaluate the safety and properties of biomaterials and relevant medical equipment [22]. It is difficult for in vitro simulations to evaluate in vivo performances because the alloying elements and coating materials affect the mechanical and corrosion properties, coatings, and experimental environments, such as different buffer systems and ions [13]. Compared to in vitro studies, animal experiments provide a closer body fluid environment to real humans; therefore, they can predict the information transformation between the experimental results and human clinical environment. Animal experiments are essential for evaluating bone repair, material properties, and host responses in the system.

Despite the wide range of clinical application prospects, evidence-based medicine seldom focuses on the surface modification of Mg alloys. Therefore, animal experiments involving widely applied conversion coatings were selected to perform a systematic review and network meta-analysis of chemical conversion coatings, such as calcium phosphate (Ca-P) conversion coating, fluoride (FLU) conversion coatings, and anodic oxidation, also known as microarc oxidation (MAO) coatings [19, 21]. Unlike a traditional literature review, this systematic review aims to perform qualitative and quantitative analyses based on relevant research [23], has strict inclusion criteria, and requires standardized instrument [24]. As far as we know, there has not been any systematic review on Mg coatings and no meta-analysis, quantitative evaluation, has been done yet. A network meta-analysis was performed to screen for magnesium alloy surface modification technologies with better comprehensive performance. The quality of the included literature was evaluated, and the evidence was graded based on the research results. Our research explored and compared the effects of magnesium alloy coating in preclinical trials and evaluated the feasibility of clinical transformation and follow-up clinical trials. The aim of this systematic review is to evaluate the surface coatings for biomedical Mg in orthopedic application with quantitative assessment.

2. Materials and Methods

2.1. PICOS

Patients: animal models with bone defect treatment, no restriction on animal species and surgical sites.

Intervention: Mg alloys with surface conversion coatings, including Ca-P conversion coating, FLU conversion coating, and MAO coating.

Comparator: Mg alloys without surface coating treatment, bare Mg (BM).

Outcomes: qualitative and quantitative analyses of the outcome indicators are shown in Figure 1.

Study design (randomized controlled trials): the specific inclusion and exclusion criteria are given in Table 1.

2.2. Literature Screening

Studies that fit these criteria were retrieved during this process. Searches were conducted on PubMed, Web of Science, and ScienceDirect databases, and a manual search was performed using Google Scholar. Table 2 provides the search strategies used in the Web of Science, and the searching strategies in other databases are given in Tables S1–S3 in Supplementary Materials. We performed the first screening in Endnote (X 9.3.1). First, the titles and abstracts were read, and duplicate studies were removed. Next, the full texts were read, and a second screening was performed based on the inclusion and exclusion criteria. The processes are shown in the PRISMA flowchart (Figure 2). Each step of the retrieval process and the results are presented in table. Literature screening was performed independently by the two authors, and divergences were resolved through discussion or consultation with another author.

2.3. Data Extraction

The general characteristics of the included studies were collected independently by two authors and then recorded on a predesigned list. Extracted data included species, ages, and weights of the animal models, types of bone defects (including fracture, osteotomy, and guided bone regeneration), types and shapes of graft materials, Mg alloy components, and the first authors of the original documents. A third author compared the consistency of the data.

2.4. Risk of Bias of Individual Studies

To assess the effectiveness of interventions in animal studies and the methodological quality of the studies, the original studies were evaluated using the Systematic Review Center for Laboratory Animal Experimentation (SYRCLE) assessment tool [25], which is a tool for evaluating the quality of animal studies based on the development of the Cochrane risk bias assessment tool [26]. We evaluated each of the 10 items using Review Manager 5.4 software. The processes were independently conducted by the two authors, and any differences were resolved through discussion or consultation with another author.

2.5. Quality of the Evidence and Risk of Bias across Studies

Given the differing nature of qualitative and quantitative evidence, we used confidence in the evidence from reviews of qualitative research (CERQual) and Grading of Recommendations Assessment, Development, and Evaluation (GRADE), respectively, to grade and evaluate the evidence obtained in this study [27–29]. The CERQual tool aims to objectively evaluate and describe the credibility of qualitative evidence review results in four aspects: method limitations, relevance, consistency, and data adequacy [27]. For network meta-analysis, based on the principal principles of GRADE, the risk of bias was integrated with the included data [30], and the GRADE tool was used to evaluate the research limitations, indirectness, inconsistency, inaccuracy, and publication bias of the evidence obtained from different outcome indicators. To assess publication bias, we created a funnel diagram for visual observations.

2.6. Data Synthesis and Network Meta-Analysis

In the network meta-analysis, we evaluated two outcome indicators: new bone formation and degradation rate (% degradation). As a continuous data variable, the standardized mean difference (SMD) was used to assess new bone formation. Two main indicators measured new bone formation: new bone volume and new bone formation rate. Although the units were not uniform, they had the same concept at different scales, so we calculated the SMDs of the included studies to evaluate new bone formation. The SMD was calculated using an appropriate 95% confidence interval (CI) for consolidation analysis. For % degradation, weighted mean differences (WMDs) were used for the statistical analysis of % degradation assessment. WMDs were calculated with appropriate 95% CIs for the synthesis analysis to evaluate % degradation.

To visualize the connection between different Mg alloy surface chemical treatment coating technologies, network evidence maps were established to determine whether there is a dominant sample study and visualize the network structure [31].

Traditional pairwise meta-analysis of all direct comparisons was conducted using a random effect model. The network estimations, which aggregated direct and indirect data estimation for each intervention, are shown in the forest plots [32]. Visual inspection of forest plots and I² measurements were used to infer the heterogeneity [33]. The mean rank and surface under the cumulative rank area (SUCRA) of different surface treatment techniques for Mg alloy were calculated [34], estimating the ranking probability of all surface coatings at each possible rank. A comprehensive comparison was conducted after mixing the results of each outcome indicator to observe the mixed effect of different coatings in vivo.

3. Results

3.1. Study Selection

Four databases were used. Three databases were searched with established search strategies, including Web of Science, PubMed, and Science Direct. We also manually searched Google Scholar based on the research purpose and the PICOS model. The specific procedure is shown in Figure 2. After filtering the title and abstract and removing the repeated literature, the full text of 106 articles was read. The included and excluded studies after first screening are given in Table S4 in Supplementary Materials. Forty-three articles were included in the systematic review, and twenty articles were included in the quantitative network meta-analysis.

3.2. Characteristics of the Included Studies

Four types of animals were included in our study: rabbits, rats, goats, and pigs; seven surgical sites were included: femur, tibia, calvaria, mandibular, ulna, radius, and ribs (Figure 3). Among all the surgical sites, the tibia is the most frequent, and among all the animals, rabbits are the most chosen.

Table 3 provides detailed information about the included studies: Mg alloy type, shape, and size, and the animal models used in the studies.

In the qualitative analysis, three directions of outcome indicators were evaluated. However, the time and assessment measurements of each outcome indicator were not identical. Forty articles concluded the influence of the materials on bone repair, forty-two articles reported the material properties after implantation, and thirty-two revealed the system response of the host.

In the quantitative analysis, twenty-one articles were included in the network meta-analysis. Among them, a total of eight articles were based on new bone formation, and sixteen articles revealed the degradation situation.

3.3. Risk of Bias within the Studies

In terms of the quality of the included studies, Figures 4 and 5 show the risk of bias within the studies. Of all the entries, random sequence generation was the biggest factor causing bias. Notably, 48.8% of all the included studies did not mention whether randomized distribution sequence methods were used, thereby generating a high risk of bias, since there is no description about the specific random grouping methods, and it is not possible to determine whether the generation methods and applications were correct. Furthermore, 18.6% of the studies showed a high risk of bias in distribution, research blinding, and other biases. This is mainly because a participant’s body part intervened in the experiment, resulting in a unit of analysis errors. The expected outcome indicators were clearly reported in all studies, and there were no selectively reported studies.

Generally, the included studies were of low quality, and incomplete experimental information resulted in high ambiguity when assessing.

3.4. Synthesis Result of Qualitative Analysis

The parameters used when manufacturing the MAO coatings are given in Table 4. Table 5 provides the manufacturing parameters of the FLU and Ca-P coatings in the included studies. The qualitative results are shown in Figure 6.

3.4.1. Orthopedic Application of FLU-Coated Mg against Bare Mg

(1)Bone repair(i)New bone formation New bone formation was described in eight studies [35–42]. Four studies indicated that FLU-coated Mg showed better new bone formation than BM [35–37, 39]. The BM had a wider range of low-density bone areas, while the FLU-coated Mg had smaller holes around it and higher bone density [36]. The tissue mineral density (TMD) and tissue mineral content (TMC) of screws in the FLU-coated Mg were better than those in BM, indicating that FLU coating had better osteoinductivity [35]. The newly formed bone trabeculae were more compact in FLU-coated Mg than in BM [37, 39]. The minor differences between the FLU-coated Mg and BM groups in two studies were not statistically significant [40, 41], and there was no indication that the FLU-coated Mg group was superior to the BM group in bone healing. New bone formation was observed in both the FLU-coated Mg and BM groups, but no comparison was made [42]. In addition, the study only described new bone formation in BM and did not elaborate on the results in FLU-coated Mg.(ii)Bone-implant contact Two studies described the bone-implant contact [35, 41]. The study demonstrated that implants have more continuous and closer contact at three months [35]. No statistically significant difference was observed between the two groups [41].(2)Material properties(i)Degradation Eight studies described the degradation of Mg alloys [35–42]. Four studies showed that the degradation performance of FLU-coated Mg was better than that of BM [35–37, 39]. In the BM group, there was obvious corrosion and fracture, whereas the FLU-coated Mg showed significantly slower degradation, and the shape remained more intact, which could provide sufficient support for the bone [37]. No statistically significant difference in reabsorption was observed between the two groups [38, 41, 42]. The study indicated that implant residues could be detected in both groups, but no comparison was made [40].(ii)Gas formation Five studies described gas formation [37–40, 42]. Less hydrogen was observed in three studies, demonstrated by the appearance of no obvious gas hole [40], no sign of gas shadow [39], and less gas release [37]. However, in another study, gas formation and absorption were described solely in case of the BM group, and the results for the FLU-coated Mg group were not reported [38]. A reduction in gas volume was observed in both groups; however, no comparison was discussed [42].(3)Systemic host responses(i)Influence on the major organs Two studies described the influence of grafts on major organs [39, 42]. The results of the FLU-coated Mg group were not specified in this study [42]. The study showed that the physiological functions of the kidney and liver were not affected by FLU-coated Mg and BM at three months, and no statistically significant difference was observed between the two groups [39].(ii)Ion concentration in serum Only one study described the ion concentration in serum [39]. The study showed that the degradation of both groups did not affect the Ca²⁺ levels in serum, and no statistically significant difference was observed for the increase in serum Mg²⁺ [39].(iii)Clinical findings Two studies described superior infection resistance in the FLU-coated Mg group compared to the BM group [35, 39]. In the BM group, inflammatory cell infiltration was observed at both one and two weeks; local bleeding was also observed. In the FLU-coated Mg group, there was only local inflammatory cell infiltration at one week, no inflammatory response and bleeding symptoms until two months, and no inflammatory response was observed at three months. The study revealed no obvious sign of inflammation in either group at three months. However, more Mg particles were swallowed by phagocytes in the BM group during the degradation process, and only a few small Mg particles were observed in the FLU-coated Mg group [39]. Five studies showed no foreign cells or signs of inflammation in the FLU-coated Mg or BM group. However, no comparison has been made in other studies [37, 38, 40–42].

3.4.2. Orthopedic Application of FLU-Coated Mg against Ca-P-Coated Mg

(1)Bone repair(i)New bone formation Two studies described new bone formation [39, 43]. One study showed that the FLU-coated Mg group exhibited better new bone formation and more compact arrangement of bone trabeculae than the Ca-P-coated Mg group at three months [39]. The trabecular number (TB. N) of the FLU-coated Mg group was significantly lower than that of the Ca-P-coated Mg group at four and eight weeks, which shows poorer bone regeneration ability of the FLU-coated Mg group than the Ca-P-coated Mg group [43].(ii)BV/TV Only one study described BV/TV [43]. The BV/TV in the FLU-coated Mg group was significantly lower than that in the Ca-P-coated Mg group at four and eight weeks [43].(2)Material properties(i)Degradation Two studies described bone implant degradation [39, 43]. One study showed that the FLU-coated Mg group degraded faster and produced a larger amount of H₂ compared with the Ca-P-coated Mg group at four and eight weeks [43]. The opposite results were obtained in another study, and the degradation rate of the FLU-coated Mg group was significantly lower than that of the Ca-P-coated Mg group at three months [39].(ii)Gas formation Two studies described gas formation [39, 43]. One study showed that a large amount of H₂ appeared in the degradation process of FLU-coated Mg at both four and eight weeks, but not in the Ca-P-coated Mg group [43]. Another study revealed that gas shadow was not observed around Mg alloy grafts in both groups, but no comparison was made [39].(3)Systemic host responses(i)Influence on the major organs Only one study described the influence of Mg alloy bone grafts on major organs [39]. Neither the FLU-coated Mg nor the Ca-P-coated Mg impacted the physiological functions of the kidney and liver at three months, and no statistically significant difference was found between the two groups.(ii)Ion concentration in serum Only one study reported ion concentrations in serum [39]. The degradation of neither the FLU-coated Mg nor the Ca-P-coated Mg affected serum Ca²⁺, and no statistically significant difference was observed for the increase in serum Mg²⁺ [39].(iii)Clinical findings Only one study reported clinical findings. No significant signs of inflammation were observed in the FLU-coated Mg and Ca-P-coated Mg groups at three months, while some small magnesium particles were observed. In addition, no comparison was made [39].

3.4.3. Orthopedic Application of Ca-P-Coated Mg against Bare Mg

(1)Bone repair effects(i)New bone formation Eleven studies described new bone formation [39, 44–53]. Four studies revealed better new bone formation in the Ca-P-coated Mg group [44, 48–50, 53]. Histological staining showed better osteoinductivity [44]. The adhesion, proliferation, and differentiation of bone cells in the Ca-P-coated Mg group were significantly enhanced [48]. The β-TCP coating has great biocompatibility and osteoconductivity on the biological surface, and more bone matrix and interconnected trabecular bone in the newly formed tissue were observed [50]. However, another study revealed opposite results: compared with the BM group, less newly formed tissue was discovered around Ca-P-coated Mg [45]. Three studies revealed that there is no sign that the Ca-P-coated Mg was better than BM in new bone formation, since there was no statistically significant difference between these two groups. Wu et al. postulated that this may have resulted from the decrease in the Ca-P coating over time [52]. Moreover, three studies revealed that new bone formation can be seen in both groups [46, 47, 51], but no comparison has been made between the two groups. The radiological healing score was used to assess the recovery conditions, and the animals in the Ca-P-coated Mg group showed better overall recovery [51].(ii)BV/TV Only one study described BV/TV [53]. During the experimental period, BV/TV of all groups increased, and Ca-P-coated Mg showed the highest BV/TV value, while BM performed worse [53].(iii)Bone-implant contact Four studies showed bone-implant contact [44, 47, 52, 54]. Only one study revealed the bone-implant contact around Ca-P-coated Mg. Coated Mg was better than that around BM. In the middle stage of the implantation, the contact between the bone tissue and implant in the coated Mg group was significantly higher than that in the BM group, while the Ca-P-coated Mg group was slightly higher in the later stage [54]. Three studies described the interface between bone tissue and implants without comparing the two groups [44, 47, 52]. In the 18 months after the operation, close contact was observed around the Ca-P-coated Mg, which indicates excellent osseointegration [44]. The formation of new bone was in close contact with the Ca-P-coated Mg, which demonstrates that the higher compatibility of the Ca-P coating to osteoblasts can lead to tight osseointegration at the implant-host tissue interface [55].(2)Material properties(i)Degradation Thirteen studies described implant degradation [39, 44–50, 52–54, 56, 57]. All studies reported that the corrosion resistance of Ca-P-coated Mg was better than that of BM. Severe corrosion was observed in the BM group, while the Ca-P-coated Mg group maintained a clear shape [39, 44–47, 50, 53, 54]. In the later stage, the hydroxyapatite-coated Mg had a relatively active degradation, indicating that in the early stage, Ca-P-coating has significant advantages in resisting absorption [49]. The residual volume of the Ca-P-coated Mg was significantly higher than that of BM [49, 52], and the average mass loss was significantly smaller than that of BM [57], indicating that Ca-P coating has a better protective effect.(ii)Gas formation Eight studies described gas formation [39, 44, 46–48, 52, 53, 56]. Less hydrogen was observed in the Ca-P-coated Mg group in five studies [44, 46, 48, 52, 56], indicated by no gas shadow [44], no obvious gas [46, 56], no voids or local accumulations formed by hydrogen [48], and smaller cavity [52]. In the remaining three studies, two revealed no bubbles [47] or gas shadow [39] in either group, and one revealed visible subcutaneous airbags on the surface of the membrane [53].(iii)Mechanical properties Three studies described the mechanical properties of the graft [51, 54, 56]. Two studies indicated that Ca-P-coated Mg exhibited better mechanical properties than BM [54, 56]. After implantation of four weeks, the tensile strength of BM was approximately half of the initial value, while Ca-P-coated Mg had a slightly smaller decrease after 12 weeks [54]. Ca-P-coated Mg can still maintain a tensile strength of >190 MPa, while the tensile strength of BM decreases rapidly after two weeks [56]. Although there is no comparison between Ca-P-coated Mg group and BM group, the treated ulna possessed biomechanical properties similar to those under normal conditions, revealing that the coated Mg alloy performed well in bone fracture surgery [51].(3)Systemic host responses(i)Ion concentration in serum Three studies described ion concentrations in serum [39, 47, 49]. The serum Mg²⁺ level in the Ca-P-coated Mg group was lower than that in the BM group [47]. Two studies showed that there were no statistically significant differences in the changes in ion concentration [39, 49]. Serum Mg²⁺ levels were in the normal range at various time periods [49]. The degradation of coated magnesium had no negative effect on the increase in serum Mg²⁺ and Ca²⁺ [39].(ii)Influence on the major organs Three studies described the influence of Ca-P-coated Mg in major organs [39, 44, 56]. It has been reported that Ca-P-coated Mg groups have less impact on major organs [56]. Two studies reported that no statistically significant difference was observed in both groups [39, 44]. The graft in both groups had no side effects on the liver and kidney functions of goats [44]. According to the hematological analysis of rabbit serum, it was found that the changes in ALT and urea in Ca-P-coated Mg and BM groups were not statistically significant. Visceral section observation revealed that the liver and kidney functions were normal, demonstrating that Ca-P coating has great in vivo biocompatibility [39].(iii)Clinical findings Seven studies described clinical findings [39, 44, 45, 49, 50, 56, 57]. Two studies revealed that Ca-P-coated Mg groups have better antiinfection ability [50, 56]. Compared with the BM group, there was no plate exposure during the experiment in the Ca-P group. Three studies revealed no infection or inflammation, and there was no significant difference between the two groups [44, 45, 49, 57]. The average animal weight in the Ca-P-coated Mg group increased, while that in the BM group decreased [57].

3.4.4. Orthopedic Application of MAO-Coated Mg Compared to Bare Mg

(1)Bone repair(i)New bone formation Twenty studies described new bone formation [11, 55, 58–75]. Fifteen studies reported that the MAO-coated Mg group was superior to the BM group [11, 55, 58–62, 65, 67, 70, 71, 73–75]. In the MAO-coated Mg group, the cortical bone healed well, and a complete fracture callus was formed while the fracture space was connected closely [58]. Histological analysis showed that the MAO-coated Mg group had more new bones [55, 59–61, 70, 71, 73–75], higher bone layer density [67], and a more perfect overall structure [62]. Osteoblasts and new bone formation were observed in the corrosion pit in the MAO-coated Mg group, whereas only stroma and fibrous tissue of fibroblasts were observed in the BM group [68]. BM significantly interfered with the growth of the physical structure of the distal femur, but not in the MAO-coated Mg group [71]. In contrast, two studies showed that new bone formation in the BM group was better than that in the MAO-coated Mg group [63, 64]. Histological examination showed that the BM had a higher bone needle maturity and better bone healing [63]. Histological analysis showed that the maturity and continuity of the trabecular bone in the BM group were higher than those in the MAO-coated Mg group, and the callus growth and fracture healing rate were also better [64]. Three studies reported bone formation in each group, but there was no comparison between the two groups [66, 69, 72].(ii)BV/TV Four studies described BV/TV [60, 70, 73, 76]. The bone mineral density around the MAO-coated Mg was much higher than that around BM [60, 73, 76]. No significant differences were found between the two groups [70].(iii)Bone-implant contact Two studies described the bone-implant contact [60, 76]. Both these studies showed that the bone contact area of implants was higher in the MAO-coated Mg group [63].(2)Material properties(i)Degradation Eighteen studies described implant degradation [11, 55, 58–70, 72, 74, 75]. Sixteen studies reported that the degradation performance of MAO-coated Mg was better than that of BM [11, 55, 58–67, 70, 72, 74, 75]. Severe corrosion occurred in the BM group, while only slight degradation occurred in the MAO-coated Mg group, and the degradation rate was significantly lower [11, 58, 63–67, 75]. By measuring the residual volume [59, 60, 70, 72] or weight loss [55, 61, 62, 74], it was found that the MAO-coated Mg group exhibited less degradation and improved corrosion resistance. In contrast, two studies reported that the degradation performance of the BM group was better than that of the MAO-coated Mg group [68, 69]. In the middle stage of the experiment, the degradation rate of the MAO-coated Mg group accelerated, resulting in the final dissolution of the implants in the MAO-coated Mg group earlier than that in the BM group [68]. In the early stage of the experiment, the degradation rate of the MAO-coated Mg group was faster than that of the BM group, whereas in the later stage, the degradation rates in both groups were accelerated. Overall, the corrosion resistance of MAO-coated Mg was better than that of BM [69].(ii)Gas formation Fourteen studies described gas formation [11, 55, 58, 60–62, 66–69, 71, 74–76]. Thirteen studies reported less gas generation in the MAO-coated Mg group than in the BM group [11, 55, 58, 60–62, 66–68, 71, 74–76]. During the experimental period, fewer bubbles were formed in the MAO-coated Mg group [61, 62, 66] and there was no obvious gas [58, 67], or the generated gas was less than that of the BM group [11, 55, 60, 69, 71, 74–76]. In addition, only one study reported the gas volumes detected at different times in the two groups, but no overall comparison was made [68].(iii)Mechanical properties Only one study conducted a three-point bending test of implants [63]. The bending strength and tensile strength of the MAO-coated Mg were significantly higher than those of BM at each follow-up time, and only the MAO-coated Mg with a thicker coating reached or even exceeded the mechanical strength of the human femur.(3)Systemic host responses(i)Influence on the major organs Four studies described the influence of Mg alloy bone implants on major organs [63, 64, 70, 73]. Three studies reported no statistical difference between the two groups [63, 64, 70]. Histological evaluation or pathological examination showed that there were no abnormal changes in the volume and shape of glomeruli, the shape of renal tubules, the arrangement of myocardial fibers, and the volume and shape of cardiomyocytes; there was no cell proliferation or necrosis. No obvious abnormalities were found in the heart and kidney tissues, indicating that there were no adverse reactions in the circulatory and urinary system [63, 64], but the structure of the hepatic sinus was damaged to a certain extent and renal interstitial hemorrhage [70]. One study reported that there is no evidence that the implants used were toxic to major organs, and no pathological changes were observed; however, no comparison was made between the two groups [73].(ii)Ion concentration in serum Ten studies described ion concentrations in serum [61–64, 66, 67, 70–72, 74]. Eight studies reported that MAO-coated Mg has a lower serum magnesium concentration than BM [61–64, 66, 67, 71, 74]. The Mg²⁺ concentration in the two groups increased with the culture time, but Mg²⁺ concentration in the BM group increased significantly more than that in the MAO-coated Mg group. The difference in serum magnesium values before and after surgery was less than that in the BM group [61–64, 66, 67, 71, 74]. One study reported that there was no significant difference in serum Mg²⁺ concentrations between the two groups [72]. Another study reported that implants did not cause metabolic disorders of major ions, such as sodium, magnesium, and calcium [70], but there was no comparison between the two groups.(iii)Clinical findings Twelve studies described clinical findings [55, 58, 60–62, 65, 68, 71, 73, 74, 76]. Six studies reported that MAO-coated Mg exhibited better antiinfectious properties than BM [55, 61, 62, 65, 71, 74]. More severe inflammatory reactions were observed in the BM group than in the MAO-coated Mg group [55, 61, 71, 74]. The high corrosion of Mg alloys produces a large amount of hydrogen and inhibits the physiological bone reaction [62]. In the BM group, rapid degradation causes the formation of absorption lacunae in bone tissue, which produces inflammation, activates osteoclasts and inhibits osteoblasts, induces osteolysis, and causes allergic reactions [65]. One study reported that there was no inflammatory reaction in each group [76]. A slight inflammatory reaction occurs in bone tissue with MAO-coated Mg, and the backbone condition of BM has not been reported [69]. No foreign body cells or signs of inflammation were observed in the two groups [58, 60, 68], and no animal death or infections occurred [73], but there were no comparisons between the two groups.

3.5. Network Structure and Results Synthesis in Network Meta-Analysis

In order to investigate the effects of different coating technologies in orthopedic applications, we conducted the experiments at different follow-up times in each original research to launch meta-analysis; this is shown in the network structure (Figure 7), which depicts the network structure of new bone formation and % degradation outcome assessment. Each dot represents an intervention, and the line between represents a direct comparison between the two different interventions. The size of the dots is proportional to the number of direct comparisons. Four interventions were included in the figure. In the degradation outcome assessment of the comparisons between each intervention, MAO is the most often used surface modification technology, while studies involving FLU treatment are limited. In the assessment of new bone outcomes, FLU treatment is the most frequently assessed coating technology. As for research on MAO coating, they seldom focused on new bone formation.

(a)

(b)

Traditional pairwise meta-analyses were conducted, and the results are shown in Figure 8 for the direct comparison in % degradation and new bone formation outcome assessment through forest plots. The three coatings exhibited excellent properties compared to BM in terms of the new bone and % degradation. However, the heterogeneity was large, indicating that the results obtained were not reliable. In addition, for both outcome assessments, the dots beyond the funnel plot indicate heterogeneity between the original studies (Figure 9).

(a)

(b)

(c)

(d)

(e)

(f)

(a)

(b)

A network meta-analysis was also performed. Figure 7 shows the interval mixture comparison between each intervention for different outcomes. Because there were no closed loops in the degradation assessment network, the consistency of the network could not be tested. The outcome assessment for new bone follows the consistency of and X² (1) = 0.63. The overall forest plots in both networks and test of inconsistency is shown in Figure 10. Figure 11 has shown the mixture estimate confidence interval of different outcome indicators. In Figure 12, the SUCRA plots showed that Ca-P coating exhibited the best degradation, followed by FLU treatment. In terms of the new bone, MAO showed the best results, while the second was Ca-P coating. The treatment ranking possibility showed the same results (Figure 13). The darker color represents better performance in the corresponding outcome. A comprehensive comparison of the four interventions shows that the Ca-P coating has the best comprehensive effect (Figure 14). The contribution plots of each direct comparison are shown in Figures S1 and S2 in Supplementary Materials.

(a)

(b)

(a)

(b)

(a)

(b)

3.6. Risk of Bias across Studies and Confidence of the Evidence

The funnel plots in Figure 9 show publication bias, which demonstrates that in terms of % degradation, other original studies have demonstrated obvious publication bias, except for the comparison involving Ca-P coating. However, in the outcome assessment of new bone formation, except for the comparison involving Ca-P coating, there was no publication bias in other original studies. The quality of the qualitative evidence is given in Table 6, and the quality of the quantitative evidence is given in Table 7.

4. Discussion

4.1. Orthopedic Application of MAO-Coated Mg Alloy

MAO coating, also known as plasma electrolytic oxidation (PEO), is a high-pressure plasma-assisted anodic oxidation process widely used in surface modification of Mg alloy [77–92]. The MAO coating process produces a unique porous structure on the surface that slows down the corrosion rate of Mg alloys, increasing the adhesion strength between implants and cells [21], and the adhesion of organic or polymer surface coatings [92]. Previous studies have demonstrated that MAO coatings have the advantages of high hardness, excellent wear resistance, moderate corrosion, good thermal stability, and dielectric properties [77, 86, 89, 90].

Normally, MAO coatings are manufactured in the oxidation reaction in electrolytes formed by NA₂SiO₃·9H₂O, KOH, and KF·2H₂O, with magnesium as the anode. The main component of the coating is magnesium oxides. The quality and chemical characteristics of MAO coatings are often influenced by the properties of the electrolyte and alloy, as well as the manufacturing process.

Figure 6 shows that in in vivo studies, compared with BM, MAO-coated Mg performs excellently in bone repair, including promoting new bone formation, increasing BV/TV, and enlarging the contact area between the bone and graft. This may result from the bubbles produced during Mg corrosion, which may inhibit physiological bone response and healing tissue formation [55]. MAO coating can also promote the material properties, which include enhancement of corrosion resistance, reduction of gas formation, and maintenance of mechanical properties during the implantation period. This degradation directly influences the mechanical strength. On the one hand, a graft with a lower degradation rate has sufficient residual volume to guarantee the mechanical strength of implants [70], whereas metal particles are produced with implant corrosion, which leads to adverse reactions, such as allergic reactions, triggering inflammation that loosens the implants [65, 71]. In addition, compared with BM, many studies have revealed that MAO-coated Mg has a better effect on the ion concentration in serum, anti-inflammation, and antiinfection, and there is no negative effect on the major organs, which indicates the great biocompatibility of MAO coatings.

However, some studies indicate that MAO coating cannot protect the alloy substrate [68, 69], which may result from the influence of surface morphology on the degradation rate. The feature morphology of the MAO coatings is a porous structure. A porous structure has both advantages and disadvantages. This structure provides a path for the electrical reaction between corrosive ions and substrates. The characteristics of pores and cracks can be seen as weak points of corrosion attack, resulting in the dense coating being corroded, which in turn exposes the Mg alloy substrate and forms a pit [68]. After the formation of pits, there is an electron effect between the coating and alloy substrate, which leads to accelerated local degradation. Therefore, the coatings were separated from the substrates when they were not completely corroded, while the BM group was protected for the accumulation of corrosion, which slows down the degradation speed [69]. Therefore, MAO coating can only protect the substrate during the limited conversion phase in the initial stage. In later immersion, degradation is accelerated owing to pores and microcracks. The pressure produced by the hydrogen and corrosion products may lead to layering. In addition, the metal compounds in the alloy may have a negative impact on the MAO coating properties, such as Mg₂Ca in Mg-Li-Ca [21].

In addition, in contrast to most research results, the MAO-coated Mg performed poorly when guiding bone restoration in the same periods, with less new bone formed [63, 64]. The protection from MAO coating led to less Mg²⁺ release and lower concentrations. As one of the bone components, Mg²⁺ can promote the deposition of calcium salts, accelerate the formation of bone, and boost fracture healing.

4.2. Orthopedic Application of Fluoride-Treated Mg Alloy

Fluorine is an indispensable trace element in the human body that promotes bone growth [93]. The FLU coating is nontoxic and chemically inert [94]. The coating process is simple and involves low cost. At room temperature (37°C), the Mg alloy samples were immersed in a hydrofluoric acid solution at a specific concentration. The thickness of the coating was related to the treatment time.

Figure 6 shows that in in vivo studies, compared with BM, FLU-coated Mg performed better in bone defect repair, including promoting new bone formation and increasing bone implant contact, which may result from fluoride stimulation in osteoblastic proliferation and promotion of mineral deposition in the cancellous bone [95]. The FLU coating can also significantly improve the material properties of Mg alloys, including enhanced corrosion resistance and reduced hydrogen generation. In terms of biocompatibility, FLU coating did not affect the serum ion concentration and major organs, and no inflammatory reaction occurred.

However, FLU coating may also have shortcomings. HF is extremely toxic; it is necessary to do a good job for safety protection [95]. H₂ is produced during HF treatment; therefore, coating is usually porous. In addition, the FLU coating thickness is insufficient to influence the desired effect [96]. These problems may be the cause of the lower performance of FLU coating compared to the other coatings.

4.3. Orthopedic Application of Ca-P-Coated Mg Alloys

Ca-P coatings have been widely used in bone implant surgery because of their superior biocompatibility, bioactivity, osteoinductivity, nontoxicity, and thermodynamic stability [47, 48]. HA(Ca₁₀(PO₄)₆(OH)₂) is the primary inorganic component of the human skeleton, which can improve the binding of the Mg matrix to the bone. After implantation, calcium and phosphorus drift off the surface of the graft and are absorbed by the body, where new tissue grows. Therefore, Ca-P has significant potential as an absorbable bone implant material [54, 97]. The coating process is simple to operate and has a high economic benefit. Mg alloy samples were prepared by immersing them in a solution of calcium salt and phosphate at a certain pH and temperature. The thickness of the coating is influenced by the treatment period. Owing to Ca/P, Mg/P, and pH, the coatings components exhibited tremendous diversity (e.g., CaHP0₄·2H₂O, Ca₁₀(PO₄)₆(OH)₂, and Ca₃(PO₄)₂).

Figure 6 shows that in in vivo studies, Ca-P-coated Mg alloys performed better in bone defect repair than BM, including promoting new bone formation and improving the BV/BT and bone implant contact rate. Ca-P coating can also significantly improve the material properties, including enhanced corrosion resistance, reduced H₂ generation, and maintenance of mechanical properties during implantation. In terms of biocompatibility, Ca-P coating did not affect serum ion concentration and major organs, and no inflammatory reaction occurred. Some studies have suggested that the Ca-P coating can improve osteoconductivity, promote differentiation of stem cells into osteoblasts, improve corrosion resistance and gas formation, and facilitate bone integration and osteoblast adhesion [44, 47]. Ca²⁺ and Mg²⁺ can also promote the proliferation of osteoblasts, inhibit bone absorption, and prevent inflammation and infection. BM was superior to Ca-P-coated Mg in terms of new bone formation during the same period, and the screw surface would be recovered with more tissue, which indicates the promotion of bone-implant contact [45]. We believe that this is due to the continuous degradation of BM and accumulation of deposition products. Under the protection of the sediment, degradation and hemolysis rates were gradually reduced. Therefore, Ca-P-coated Mg was better at new bone formation within a short period of time, but the results over longer periods of time require further observation and analysis.

The disadvantage of Ca-P coating is regulation difficulty; the formation of a specified coating requires accurate adjustments of Ca/P, Mg/P, and pH. In addition, it is very difficult to increase the content [21].

4.4. Previous and International Research Progress

Biodegradable Mg alloys have great clinical prospects as an ideal biomaterial for orthopedic applications. However, relevant meta-analyses and systematic reviews were limited, and previous studies simply focused on whether the Mg alloy has the same effect as materials frequently used clinically, such as titanium alloys.

Zhang et al. conducted a systematic review and meta-analysis to investigate the bone defect repair properties of biodegradable metals (pure magnesium, magnesium alloy, pure zinc, and zinc alloy) in animal models, but the results showed that the evidence quality was low, and some other biodegradable metals did not show good bone repair ability [98]. Sukotjo et al. compared the complications after osteosurgical treatment by introducing Mg or Ti screws with metal plates, and the results showed that Mg screws have a similar effect to Ti screw [99].

Sun et al. studied the effects of Mg bone implants in fracture animal models with a systematic review to affirm the positive role of Mg in bone fracture healing [100]. The lack of a standardized animal model and high heterogeneity made it difficult to perform a meta-analysis. Feeley et al. reviewed the application of different biodegradable materials in bone fixation, such as poly L-lactic acid, polyglycolide, and Mg [101]. Most Mg implants have similar clinical effects to titanium alloys, and only one study had to be removed due to severe synovitis. The effect of Mg screws in patients with immature bone growth in orthopedic surgeries was analyzed by Baldini et al. who showed that there was no negative reaction in patients using Mg screws with significant clinical effects and radiological assessment, which indicates a stable fixation effect given by Mg screws [102]. However, there have been few systematic reviews and meta-analyses of surface coatings.

4.5. Animal Experiments

In vitro experiments have the advantages of a short experimental cycle, easy control of experimental conditions, and good repeatability. However, in vitro experiments cannot completely simulate a complex environment, and the standards are not uniform. For example, the quality of various experimental methods cannot be evaluated, and the selection of simulated body fluids varies. Therefore, we selected animal experiments for analysis and evaluated the bone repair ability of Mg alloy implants with different coatings in vivo.

Some of the studies in this work followed the selection criteria of animal experiments, which is conducive to reducing the influence of individual differences in animals. In the selection of animal models for bone defects, 28 studies used rabbits, 12 used rats, 3 used pigs, and 1 used goat models. Rabbits and rats have been widely used in preclinical experiments. They are cheap, fast growing, easy to feed, and easy to operate. However, the bone healing and load-bearing capacity of these animals are quite different from those of humans, which may lead to deviation from clinical practice. For example, rabbits are much smaller in weight and load capacity than humans, but their bone metabolism is three times that of humans [103]. Compared with rabbits, the skeletal structure of goats is more similar to that of the human body, which is more meaningful for clinical transformation [44]. Human-sized implants can be implanted in pigs, where the soft tissue properties and wound-healing properties of the face and skull are similar to those of humans [60].

The types of surgery were mostly bone defects in the included studies. There were only five fractures, three osteotomies, and two guided bone regeneration. The extent of bone defects caused by surgery is mostly suitable for the size of implants, and different animal models have their own characteristic bone defects. Most surgeries are selected in the femur for reasons, such as simple operation and strong recovery ability. Meanwhile, as an important weight-bearing bone, the postoperative healing of the femur can be used as an important indicator of the bone repair ability of Mg alloy implants, which is of great significance for clinical application.

We conducted a comprehensive statistical analysis, which has good clinical significance and a reference value for the selection of different Mg alloy coatings. However, the final analysis may be affected to some extent by different animal models and surgical types.

4.6. Resources of Heterogeneity

The forest plot indicates that the comparison of new bone formation between the FLU and Ca-P-coated Mg alloys showed low heterogeneity, and the other comparisons showed high heterogeneity. This may be due to the different follow-up times, as the material degrades over time and becomes less supportive of the bone. Studies have shown that a qualified plate for fracture repair may not begin absorption until at least six weeks after surgery [104]. We included different animal species, experimental sites, chemical composition, and scaffold structure, which may have resulted in different healing rates [105]. In addition, we could not unify the variables for the Mg alloy substrates. Studies revealed that different Mg alloy substrates and Mg alloys containing different metal ratios may lead to different degradation rates and new bone formation [106–108].

4.7. Risk of Bias and Quality of the Evidence

The SYRCLE tool was applied to perform risk of bias assessment in the included studies [25]. Meanwhile, the CERQual and GRADE tools were applied to evaluate qualitative and quantitative evidence [27–29]. Quality assessment through these methods can be used to assess the reliability of results and the probability of future clinical transformation.

The design, process, and outcome assessment can lead to biases and, therefore, the facticity of the studies. The results demonstrate that the included studies were not of high quality. None of the included studies described their grouping process in detail, so our confidence in the overall evidence was low. Most animal studies have small sample sizes, which would result in differences in the baseline. The similarity of the baseline characteristics affects the comparability of our study. Only a small number of the studies showed similar baseline characteristics, one showed dissimilarity, and majority of the studies were not mentioned in detail. The placement of animals and whether the selection of animals is random also influences the reliability of experimental results. If animals were raised in the same environment, the nonrandom environment did not affect the results of the experiment, even though the allocation was not random [25]. Selectively reporting the animal research results can cause publication bias, which may influence the reliability of the experimental results and even produce publications with conflicting conclusions [109].

In addition, we found that the clinical transformation of the included studies was affected by implantation time, coating manufacturing parameters, individual characteristics of animal models, implant size and shape, surgical sites, and number and follow-up time of the experiments. A small number of animals also reduced our confidence in the overall evidence. We were not sure whether studies in other settings or populations would show similar results, which requires further discussion and analysis [27].

4.8. Limitations and Innovation

In vivo experiments were selected as research objects because of their contribution to clinical diagnosis and treatment. Conversion coatings are a popular and common coating method. To study the specificity, deposition coating and other methods have been abandoned. The authors selected different experimental sites, sample characteristics, and time groups in different studies. All these factors may have affected the results of our analysis. More than 600 articles were included in the first round of selection, and only forty-three were selected for analysis and discussion. The lack of research will be improved with the passage of time and development in the research in this field. In addition, there was no closed network in the meta-analysis in the assessment of % degradation, so we could not detect its consistency.

However, we specifically considered the coating corrosion features and their effects on new bone formation in animals for network meta-analysis. This is the first study to include material responses to the host system in qualitative outcome assessment, which will be of great significance for clinical contribution.

4.9. Inspiration for Future Research

Surface modification is the main method used to optimize the corrosion properties of Mg alloys. We believe that future work could focus on the following aspects to investigate perfect coatings for clinical research. First, the selection of coating materials and manufacturing technologies can be applied to promote the corrosion resistance and biocompatibility of Mg alloy implants. In terms of mechanical properties, the porosity and thickness of the coating can be a new direction for investigation. Composite coatings combined with multiple technologies have good development prospects. Second, the diversity of surgical models, different operation procedures and specific parameters of coating, various measurement methods, and data collection types lead to unsatisfactory results in this analysis and data synthesis from different studies. We hope to unify research standards to improve subsequent research. Finally, the surface modification technology of magnesium alloys is developing in the direction of environmental protection, high efficiency, and customization. In future clinical applications, different coating materials and coating methods can be selected according to different clinical requirements to achieve personalized treatment.

5. Conclusions

The qualitative analysis proved that MAO-coated, fluoride-treated, and Ca-P-coated Mg alloys performed excellently in orthopedic applications. These three surface coatings have excellent material properties and biocompatibility. Compared with the bare Mg alloy, the coated alloy can promote bone healing. The quantitative analysis demonstrated that MAO coating can significantly increase new bone formation, and Ca-P coating can notably enhance the corrosion resistance. Even though the included studies were of relatively low quality due to selection bias, which influenced the credibility of our results to some degree, this study is still the first one that carried out quantitative analysis on surface coatings for biomedical Mg.

Data Availability

The data used to support the findings of this research are included within the article and are labeled with references.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Authors’ Contributions

XinYue Lu, HongXin Cai, and Yu Ru Li contributed equally to this work.

Supplementary Materials

Figure S1. Contribution graph of % degradation. Figure S2. Contribution graph of new bone formation. Table S1. Searching strategy and result on the PubMed. Table S2. Searching strategy and result on Science Direct. Table S3. Searching strategy and result on Web of Science. Table S4. Included and excluded studies after first screening. (Supplementary Materials)

References

H. Gao, M. Zhang, J. Zhao, L. Gao, and M. Li, “In vitro and in vivo degradation and mechanical properties of ZEK100 magnesium alloy coated with alginate, chitosan and mechano-growth factor,” Materials Science and Engineering: C, Materials for Biological Applications, vol. 63, pp. 450–461, 2016.
View at: Publisher Site | Google Scholar
Z. Gao, M. Song, R.-L. Liu et al., “Improving in vitro and in vivo antibacterial functionality of Mg alloys through micro-alloying with Sr and Ga,” Materials Science and Engineering: C, Materials for Biological Applications, vol. 104, Article ID 109926, 2019.
View at: Publisher Site | Google Scholar
J. Chen, L. Tan, X. Yu, I. P. Etim, M. Ibrahim, and K. Yang, “Mechanical properties of magnesium alloys for medical application: a review,” Journal of the Mechanical Behavior of Biomedical Materials, vol. 87, pp. 68–79, 2018.
View at: Publisher Site | Google Scholar
O. Böstman and H. Pihlajamäki, “Clinical biocompatibility of biodegradable orthopaedic implants for internal fixation: a review,” Biomaterials, vol. 21, pp. 2615–2621, 2000.
View at: Publisher Site | Google Scholar
M. L. Busam, R. J. Esther, and W. T. Obremskey, “Hardware removal: indications and expectations,” Journal of the American Academy of Orthopaedic Surgeons, vol. 14, no. 2, pp. 113–120, 2006.
View at: Publisher Site | Google Scholar
R. I. M. Asri, W. S. W. Harun, M. Samykano et al., “Corrosion and surface modification on biocompatible metals: a review,” Materials Science and Engineering: C, vol. 77, pp. 1261–1274, 2017.
View at: Publisher Site | Google Scholar
N. Espallargas, C. Torres, and A. I. Muñoz, “A metal ion release study of CoCrMo exposed to corrosion and tribocorrosion conditions in simulated body fluids,” Wear, vol. 332-333, pp. 669–678, 2015.
View at: Publisher Site | Google Scholar
G. Li, L. Zhang, L. Wang et al., “Dual modulation of bone formation and resorption with zoledronic acid-loaded biodegradable magnesium alloy implants improves osteoporotic fracture healing: an in vitro and in vivo study,” Acta Biomaterialia, vol. 65, pp. 486–500, 2018.
View at: Publisher Site | Google Scholar
C. Chanlalit, D. R. Shukla, J. S. Fitzsimmons, K.-N. An, and S. W. O’Driscoll, “Stress shielding around radial head prostheses,” Journal of Hand Surgery, vol. 37, no. 10, pp. 2118–2125, 2012.
View at: Publisher Site | Google Scholar
X. Gao, C. Y. Dai, Q. Jia et al., “In vivo corrosion behavior of biodegradable magnesium alloy by MAF treatment,” Scanning, vol. 2021, Article ID 5530788, 9 pages, 2021.
View at: Publisher Site | Google Scholar
M. H. Song, W. J. Yoo, T.-J. Cho, Y. K. Park, W.-J. Lee, and I. H. Choi, “In vivo response of growth plate to biodegradable Mg-Ca-Zn alloys depending on the surface modification,” International Journal of Molecular Sciences, vol. 20, no. 15, p. 3761, 2019.
View at: Publisher Site | Google Scholar
H.-S. Han, S. Loffredo, I. Jun et al., “Current status and outlook on the clinical translation of biodegradable metals,” Materials Today, vol. 23, pp. 57–71, 2019.
View at: Publisher Site | Google Scholar
S. Agarwal, J. Curtin, B. Duffy, and S. Jaiswal, “Biodegradable magnesium alloys for orthopaedic applications: a review on corrosion, biocompatibility and surface modifications,” Materials Science and Engineering: C, vol. 68, pp. 948–963, 2016.
View at: Publisher Site | Google Scholar
Y.-T. Chen, F.-Y. Hung, Y.-L. Lin, and C.-Y. Lin, “Biodegradation ZK50 magnesium alloy compression screws: mechanical properties, biodegradable characteristics and implant test,” Journal of Orthopaedic Science, vol. 25, no. 6, pp. 1107–1115, 2020.
View at: Publisher Site | Google Scholar
X. J. Wang, D. K. Xu, R. Z. Wu et al., “What is going on in magnesium alloys?” Journal of Materials Science & Technology, vol. 34, no. 2, pp. 245–247, 2018.
View at: Publisher Site | Google Scholar
E. Ghali, W. Dietzel, and K.-U. Kainer, “General and localized corrosion of magnesium alloys: a critical review,” Journal of Materials Engineering and Performance, vol. 13, no. 1, pp. 7–23, 2004.
View at: Publisher Site | Google Scholar
G. L. Song and A. Atrens, “Corrosion mechanisms of magnesium alloys,” Advanced Engineering Materials, vol. 1, no. 1, pp. 11–33, 1999.
View at: Publisher Site | Google Scholar
D. Zhang, F. Peng, and X. Liu, “Protection of magnesium alloys: from physical barrier coating to smart self-healing coating,” Journal of Alloys and Compounds, vol. 853, Article ID 157010, 2021.
View at: Publisher Site | Google Scholar
H. Hornberger, S. Virtanen, and A. R. Boccaccini, “Biomedical coatings on magnesium alloys - a review,” Acta Biomaterialia, vol. 8, no. 7, pp. 2442–2455, 2012.
View at: Publisher Site | Google Scholar
P. Tian and X. Liu, “Surface modification of biodegradable magnesium and its alloys for biomedical applications,” Regenerative Biomaterials, vol. 2, no. 2, pp. 135–151, 2015.
View at: Publisher Site | Google Scholar
Z.-Z. Yin, W.-C. Qi, R.-C. Zeng et al., “Advances in coatings on biodegradable magnesium alloys,” Journal of Magnesium and Alloys, vol. 8, no. 1, pp. 42–65, 2020.
View at: Publisher Site | Google Scholar
C. R. Hooijmans, R. B. M. de Vries, M. Ritskes-Hoitinga et al., “Facilitating healthcare decisions by assessing the certainty in the evidence from preclinical animal studies,” PLoS One, vol. 13, no. 1, Article ID e0187271, 2018.
View at: Publisher Site | Google Scholar
A. Harden and J. Thomas, “Methodological issues in combining diverse study types in systematic reviews,” International Journal of Social Research Methodology, vol. 8, no. 3, pp. 257–271, 2005.
View at: Publisher Site | Google Scholar
E. Aromataris and A. Pearson, “The systematic review,” AJN, American Journal of Nursing, vol. 114, no. 3, pp. 53–58, 2014.
View at: Publisher Site | Google Scholar
C. R. Hooijmans, M. M. Rovers, R. B. de Vries, M. Leenaars, M. Ritskes-Hoitinga, and M. W. Langendam, “SYRCLE’s risk of bias tool for animal studies,” BMC Medical Research Methodology, vol. 14, no. 1, p. 43, 2014.
View at: Publisher Site | Google Scholar
J. P. T. Higgins, D. G. Altman, P. C. Gotzsche et al., “The Cochrane Collaboration’s tool for assessing risk of bias in randomised trials,” BMJ, vol. 343, no. 2, Article ID d5928, 2011.
View at: Publisher Site | Google Scholar
S. Lewin, C. Glenton, H. Munthe-Kaas et al., “Using qualitative evidence in decision making for health and social interventions: an approach to assess confidence in findings from qualitative evidence syntheses (GRADE-CERQual),” PLoS Medicine, vol. 12, no. 10, Article ID e1001895, 2015.
View at: Publisher Site | Google Scholar
G. Langer, J. J. Meerpohl, M. Perleth, G. Gartlehner, A. Kaminski-Hartenthaler, and H. Schünemann, “GRADE-leitlinien: 1. einführung - GRADE-evidenzprofile und summary-of-findings-tabellen,” Zeitschrift für Evidenz, Fortbildung und Qualität im Gesundheitswesen, vol. 106, no. 5, pp. 357–368, 2012.
View at: Publisher Site | Google Scholar
G. H. Guyatt, A. D. Oxman, G. E. Vist et al., “GRADE: an emerging consensus on rating quality of evidence and strength of recommendations,” BMJ, vol. 336, no. 7650, pp. 924–926, 2008.
View at: Publisher Site | Google Scholar
G. Salanti, C. Del Giovane, A. Chaimani, D. M. Caldwell, and J. P. T. Higgins, “Evaluating the quality of evidence from a network meta-analysis,” PLoS One, vol. 9, no. 7, Article ID e99682, 2014.
View at: Publisher Site | Google Scholar
C. B. Winder, J. M. Sargeant, D. Hu et al., “Comparative efficacy of antimicrobials for treatment of clinical mastitis in lactating dairy cattle: a systematic review and network meta-analysis,” Animal Health Research Reviews, vol. 20, no. 2, pp. 229–246, 2019.
View at: Publisher Site | Google Scholar
U. Krahn, H. Binder, and J. König, “A graphical tool for locating inconsistency in network meta-analyses,” BMC Medical Research Methodology, vol. 13, no. 1, p. 35, 2013.
View at: Publisher Site | Google Scholar
A. Chaimani, J. P. T. Higgins, D. Mavridis, P. Spyridonos, and G. Salanti, “Graphical tools for network meta-analysis in STATA,” PLoS One, vol. 8, no. 10, Article ID e76654, 2013.
View at: Publisher Site | Google Scholar
G. Salanti, A. E. Ades, and J. P. A. Ioannidis, “Graphical methods and numerical summaries for presenting results from multiple-treatment meta-analysis: an overview and tutorial,” Journal of Clinical Epidemiology, vol. 64, no. 2, pp. 163–171, 2011.
View at: Publisher Site | Google Scholar
W. Sun, G. Zhang, L. Tan, K. Yang, and H. Ai, “The fluoride coated AZ31B magnesium alloy improves corrosion resistance and stimulates bone formation in rabbit model,” Materials Science and Engineering: C, Materials for Biological Application, vol. 63, pp. 506–511, 2016.
View at: Publisher Site | Google Scholar
H. Jiang, J. Wang, M. Chen, and D. Liu, “Biodegradable magnesium alloys for orthopaedic applications: a review on corrosion, biocompatibility and surface modifications,” Materials Science and Engineering: C, vol. 75, pp. 1068–1074, 2017.
View at: Publisher Site | Google Scholar
Z. Li, S. Shizhao, M. Chen, B. D. Fahlman, L. Debao, and H. Bi, “In vitro and in vivo corrosion, mechanical properties and biocompatibility evaluation of MgF 2 -coated Mg-Zn-Zr alloy as cancellous screws,” Materials Science and Engineering: C, Materials for Biological Applications, vol. 75, pp. 1268–1280, 2017.
View at: Publisher Site | Google Scholar
C. Iglesias, O. G. Bodelón, R. Montoya et al., “Fracture bone healing and biodegradation of AZ31 implant in rats,” Biomedical Materials, vol. 10, no. 2, Article ID 025008, 2015.
View at: Publisher Site | Google Scholar
J. e. Sun, J. Wang, H. Jiang, M. Chen, Y. Bi, and D. Liu, “In vivo comparative property study of the bioactivity of coated Mg-3Zn-0.8Zr alloy,” Materials Science and Engineering: C, Materials for Bilogical Applications, vol. 33, no. 6, pp. 3263–3272, 2013.
View at: Publisher Site | Google Scholar
M. Barbeck, L. Kühnel, F. Witte et al., “Degradation, bone regeneration and tissue response of an innovative volume stable magnesium-supported GBR/GTR barrier membrane,” International Journal of Molecular Sciences, vol. 21, no. 9, p. 3098, 2020.
View at: Publisher Site | Google Scholar
H. Naujokat, C. B. Ruff, T. Klüter, J.-M. Seitz, Y. Açil, and J. Wiltfang, “Influence of surface modifications on the degradation of standard-sized magnesium plates and healing of mandibular osteotomies in miniature pigs,” International Journal of Oral and Maxillofacial Surgery, vol. 49, no. 2, pp. 272–283, 2020.
View at: Publisher Site | Google Scholar
O. G. Bodelón, C. Iglesias, J. Garrido, C. Clemente, M. C. Garcia-Alonso, and M. L. Escudero, “Analysis of metallic traces from the biodegradation of endomedullary AZ31 alloy temporary implants in rat organs after long implantation times,” Biomedical Materials, vol. 10, no. 4, Article ID 045015, 2015.
View at: Publisher Site | Google Scholar
W. Wang, G. Jia, Q. Wang et al., “The in vitro and in vivo biological effects and osteogenic activity of novel biodegradable porous Mg alloy scaffolds,” Materials & Design, vol. 189, Article ID 108514, 2020.
View at: Publisher Site | Google Scholar
X. Kong, L. Wang, G. Li et al., “Mg-based bone implants show promising osteoinductivity and controllable degradation: a long-term study in a goat femoral condyle fracture model,” Materials Science and Engineering: C,Materials for Biologiacl Applications, vol. 86, pp. 42–47, 2018.
View at: Publisher Site | Google Scholar
Q. Wang, L. Tan, W. Xu, B. Zhang, and K. Yang, “Dynamic behaviors of a Ca-P coated AZ31B magnesium alloy during in vitro and in vivo degradations,” Materials Science and Engineering: B, vol. 176, no. 20, pp. 1718–1726, 2011.
View at: Publisher Site | Google Scholar
J. Niu, G. Yuan, Y. Liao et al., “Enhanced biocorrosion resistance and biocompatibility of degradable Mg-Nd-Zn-Zr alloy by brushite coating,” Materials Science and Engineering: C, vol. 33, no. 8, pp. 4833–4841, 2013.
View at: Publisher Site | Google Scholar
J. X. Yang, F. Z. Cui, I.-S. Lee et al., “In vivo biocompatibility and degradation behavior of Mg alloy coated by calcium phosphate in a rabbit model,” Journal of Biomaterials Applications, vol. 27, no. 2, pp. 153–164, 2012.
View at: Publisher Site | Google Scholar
Y. Husak, O. Solodovnyk, A. Yanovska et al., “Degradation and in vivo response of hydroxyapatite-coated Mg alloy,” Coatings, vol. 8, no. 11, p. 375, 2018.
View at: Publisher Site | Google Scholar
H.-K. Lim, S.-H. Byun, J.-Y. Lee et al., “Radiological, histological, and hematological evaluation of hydroxyapatite-coated resorbable magnesium alloy screws placed in rabbit tibia,” Journal of Biomedical Materials Research Part B: Applied Biomaterials, vol. 105, no. 6, pp. 1636–1644, 2017.
View at: Publisher Site | Google Scholar
H. Chai, L. Guo, X. Wang et al., “In vitro and in vivo evaluations on osteogenesis and biodegradability of a β-tricalcium phosphate coated magnesium alloy,” Journal of Biomedical Materials Research Part A, vol. 100, no. 2, pp. 293–304, 2012.
View at: Publisher Site | Google Scholar
M. R. Smith, P. Atkinson, D. White et al., “Design and assessment of a wrapped cylindrical Ca-P AZ31 Mg alloy for critical-size ulna defect repair,” Journal of Biomedical Materials Research Part B: Applied Biomaterials, vol. 100, no. 1, pp. 206–216, 2012.
View at: Publisher Site | Google Scholar
S. Wu, Y.-S. Jang, and M.-H. Lee, “Enhancement of bone regeneration on calcium-phosphate-coated magnesium mesh: using the rat calvarial model,” Frontiers in Bioengineering and Biotechnology, vol. 9, Article ID 652334, 2021.
View at: Publisher Site | Google Scholar
W. Peng, J.-X. Chen, X.-F. Shan et al., “Mg-based absorbable membrane for guided bone regeneration (GBR): a pilot study,” Rare Metals, vol. 38, no. 6, pp. 577–587, 2019.
View at: Publisher Site | Google Scholar
S.-M. Kim, J.-H. Jo, S.-M. Lee et al., “Hydroxyapatite-coated magnesium implants with improved in vitro and in vivo biocorrosion, biocompatibility, and bone response,” Journal of Biomedical Materials Research Part A, vol. 102, no. 2, pp. 429–441, 2014.
View at: Publisher Site | Google Scholar
M. Razavi, M. Fathi, O. Savabi, L. Tayebi, and D. Vashaee, “Biodegradable magnesium bone implants coated with a novel bioceramic nanocomposite,” Materials, vol. 13, no. 6, p. 1315, 2020.
View at: Publisher Site | Google Scholar
H.-K. Lim, S.-H. Byun, J.-M. Woo et al., “Biocompatibility and biocorrosion of hydroxyapatite-coated magnesium plate: animal experiment,” Materials, vol. 10, no. 10, p. 1149, 2017.
View at: Publisher Site | Google Scholar
X. Xiao, H. Yu, Q. Zhu, G. Li, Y. Qu, and R. Gu, “In vivo corrosion resistance of Ca-P coating on AZ60 magnesium alloy,” Journal of Bionic Engineering, vol. 10, no. 2, pp. 156–161, 2013.
View at: Publisher Site | Google Scholar
J. Han, P. Wan, Y. Ge et al., “Tailoring the degradation and biological response of a magnesium-strontium alloy for potential bone substitute application,” Materials Science and Engineering: C, Materials for Biological. Applications, vol. 58, pp. 799–811, 2016.
View at: Publisher Site | Google Scholar
Y.-K. Kim, Y.-S. Jang, S.-Y. Kim, and M.-H. Lee, “Functions achieved by the hyaluronic acid derivatives coating and hydroxide film on bio-absorbed Mg,” Applied Surface Science, vol. 473, pp. 31–39, 2019.
View at: Publisher Site | Google Scholar
B. Schaller, N. Saulacic, T. Imwinkelried et al., “In vivo degradation of magnesium plate/screw osteosynthesis implant systems: soft and hard tissue response in a calvarial model in miniature pigs,” Journal of Cranio-Maxillofacial Surgery, vol. 44, no. 3, pp. 309–317, 2016.
View at: Publisher Site | Google Scholar
M. Razavi, M. Fathi, O. Savabi, D. Vashaee, and L. Tayebi, “In vivo study of nanostructured akermanite/PEO coating on biodegradable magnesium alloy for biomedical applications,” Journal of Biomedical Materials Research Part A, vol. 103, no. 5, pp. 1798–1808, 2015.
View at: Publisher Site | Google Scholar
M. Razavi, M. Fathi, O. Savabi et al., “In vivo study of nanostructured diopside (CaMgSi2O6) coating on magnesium alloy as biodegradable orthopedic implants,” Applied Surface Science, vol. 313, pp. 60–66, 2014.
View at: Publisher Site | Google Scholar
J. Zhuang, Y. Jing, Y. Wang, J. Zhang, H. Xie, and J. Yan, “Degraded and osteogenic properties of coated magnesium alloy AZ31; an experimental study,” Journal of Orthopaedic Surgery and Research, vol. 11, no. 1, p. 30, 2016.
View at: Publisher Site | Google Scholar
Y. F. Wu, Y. M. Wang, Y. B. Jing et al., “In vivo study of microarc oxidation coated biodegradable magnesium plate to heal bone fracture defect of 3 mm width,” Colloids and Surfaces B: Biointerfaces, vol. 158, pp. 147–156, 2017.
View at: Publisher Site | Google Scholar
J. Han, P. Wan, Y. Sun et al., “Fabrication and evaluation of a bioactive Sr-Ca-P contained Micro-Arc oxidation coating on magnesium strontium alloy for bone repair application,” Journal of Materials Science & Technology, vol. 32, no. 3, pp. 233–244, 2016.
View at: Publisher Site | Google Scholar
Y. Wu, Y. M. Wang, D. W. Zhao et al., “In vivo study of microarc oxidation coated Mg alloy as a substitute for bone defect repairing: degradation behavior, mechanical properties, and bone response,” Colloids and Surfaces B: Biointerfaces, vol. 181, pp. 349–359, 2019.
View at: Publisher Site | Google Scholar
H. Xu, T. Hu, M. Wang et al., “Degradability and biocompatibility of magnesium-MAO: the consistency and contradiction between in-vitro and in-vivo outcomes,” Arabian Journal of Chemistry, vol. 13, no. 1, pp. 2795–2805, 2020.
View at: Publisher Site | Google Scholar
S. F. Fischerauer, T. Kraus, X. Wu et al., “In vivo degradation performance of micro-arc-oxidized magnesium implants: a micro-CT study in rats,” Acta Biomaterialia, vol. 9, no. 2, pp. 5411–5420, 2013.
View at: Publisher Site | Google Scholar
X. Lin, L. Tan, Q. Wang, G. Zhang, B. Zhang, and K. Yang, “In vivo degradation and tissue compatibility of ZK60 magnesium alloy with micro-arc oxidation coating in a transcortical model,” Materials Science and Engineering: C, vol. 33, no. 7, pp. 3881–3888, 2013.
View at: Publisher Site | Google Scholar
J. Wang, F. Peng, X. Wu et al., “Biocompatibility and bone regeneration of PEO/Mg-Al LDH-coated pure Mg: an in vitro and in vivo study,” Science China Materials, vol. 64, no. 2, pp. 460–473, 2021.
View at: Publisher Site | Google Scholar
M. Razavi, M. Fathi, O. Savabi, D. Vashaee, and L. Tayebi, “In vivo assessments of bioabsorbable AZ91 magnesium implants coated with nanostructured fluoridated hydroxyapatite by MAO/EPD technique for biomedical applications,” Materials Science and Engineering: C, Materials for Boilogical Applications, vol. 48, pp. 21–27, 2015.
View at: Publisher Site | Google Scholar
C.-y. Bai, J.-w. Li, W.-b. Ta, B. Li, and Y. Han, “In vivo study on the corrosion behavior of magnesium alloy surface treated with micro-arc oxidation and hydrothermal deposition,” Orthopaedic Surgery, vol. 9, no. 3, pp. 296–303, 2017.
View at: Publisher Site | Google Scholar
W. Liu, T. Li, C. Yang et al., “Lithium-incorporated nanoporous coating formed by micro arc oxidation (MAO) on magnesium alloy with improved corrosion resistance, angiogenesis and osseointegration,” Journal of Biomedical Nanotechnology, vol. 15, no. 6, pp. 1172–1184, 2019.
View at: Publisher Site | Google Scholar
M. Razavi, M. Fathi, O. Savabi, D. Vashaee, and L. Tayebi, “In vivo biocompatibility of Mg implants surface modified by nanostructured merwinite/PEO,” Journal of Materials Science: Materials in Medicine, vol. 26, no. 5, p. 184, 2015.
View at: Publisher Site | Google Scholar
N. Zhang, D. Zhao, N. Liu et al., “Assessment of the degradation rates and effectiveness of different coated Mg-Zn-Ca alloy scaffolds for in vivo repair of critical-size bone defects,” Journal of Materials Science: Materials in Medicine, vol. 29, no. 9, p. 138, 2018.
View at: Publisher Site | Google Scholar
B. Schaller, N. Saulacic, S. Beck et al., “Osteosynthesis of partial rib osteotomy in a miniature pig model using human standard-sized magnesium plate/screw systems: effect of cyclic deformation on implant integrity and bone healing,” Journal of Cranio-Maxillofacial Surgery, vol. 45, no. 6, pp. 862–871, 2017.
View at: Publisher Site | Google Scholar
C. Blawert, W. Dietzel, E. Ghali, and G. Song, “Anodizing treatments for magnesium alloys and their effect on corrosion resistance in various environments,” Advanced Engineering Materials, vol. 8, no. 6, pp. 511–533, 2006.
View at: Publisher Site | Google Scholar
G. P. Wirtz, S. D. Brown, and W. M. Kriven, “Anodizing treatments for magnesium alloys and their effect on corrosion resistance in various environments,” Materials and Manufacturing Processes, vol. 6, no. 1, pp. 87–115, 1991.
View at: Publisher Site | Google Scholar
Y. Ma, X. Nie, D. O. Northwood, and H. Hu, “Corrosion and erosion properties of silicate and phosphate coatings on magnesium,” Thin Solid Films, vol. 469-470, pp. 472–477, 2004.
View at: Publisher Site | Google Scholar
H. F. Guo and M. Z. An, “Growth of ceramic coatings on AZ91D magnesium alloys by micro-arc oxidation in aluminate-fluoride solutions and evaluation of corrosion resistance,” Applied Surface Science, vol. 246, no. 1–3, pp. 229–238, 2005.
View at: Publisher Site | Google Scholar
H. F. Guo, M. Z. An, H. B. Huo, S. Xu, and L. J. Wu, “Microstructure characteristic of ceramic coatings fabricated on magnesium alloys by micro-arc oxidation in alkaline silicate solutions,” Applied Surface Science, vol. 252, no. 22, pp. 7911–7916, 2006.
View at: Publisher Site | Google Scholar
J. Liang, L. Hu, and J. Hao, “Improvement of corrosion properties of microarc oxidation coating on magnesium alloy by optimizing current density parameters,” Applied Surface Science, vol. 253, no. 16, pp. 6939–6945, 2007.
View at: Publisher Site | Google Scholar
A. Ghasemi, V. S. Raja, C. Blawert, W. Dietzel, and K. U. Kainer, “Study of the structure and corrosion behavior of PEO coatings on AM50 magnesium alloy by electrochemical impedance spectroscopy,” Surface and Coatings Technology, vol. 202, no. 15, pp. 3513–3518, 2008.
View at: Publisher Site | Google Scholar
J. Liu, Y. Lu, X. Jing, Y. Yuan, and M. Zhang, “Characterization of plasma electrolytic oxidation coatings formed on Mg-Li alloy in an alkaline silicate electrolyte containing silica sol,” Materials and Corrosion, vol. 60, no. 11, pp. 865–870, 2009.
View at: Publisher Site | Google Scholar
U. Malayoglu, K. C. Tekin, and S. Shrestha, “Influence of post-treatment on the corrosion resistance of PEO coated AM50B and AM60B Mg alloys,” Surface and Coatings Technology, vol. 205, no. 6, pp. 1793–1798, 2010.
View at: Publisher Site | Google Scholar
Z. P. Yao, L. L. Li, X. R. Liu, and Z. H. Jiang, “Preparation of ceramic conversion layers containing Ca and P on AZ91D Mg alloys by plasma electrolytic oxidation,” Surface Engineering, vol. 26, no. 5, pp. 317–320, 2010.
View at: Publisher Site | Google Scholar
W. Liangcai, W. Zhiming, L. Xiangtong, and Z. Shuyuan, in Proceedings of the 2010 Second International Workshop on Education Technology and Computer Science, pp. 810–812, Wuhan, China, March 2010.
X. G. Han, X. P. Zhu, and M. K. Lei, “Electrochemical properties of microarc oxidation films on a magnesium alloy modified by high-intensity pulsed ion beam,” Surface and Coatings Technology, vol. 206, no. 5, pp. 874–878, 2011.
View at: Publisher Site | Google Scholar
R. O. Hussein, P. Zhang, X. Nie, Y. Xia, and D. O. Northwood, “The effect of current mode and discharge type on the corrosion resistance of plasma electrolytic oxidation (PEO) coated magnesium alloy AJ62,” Surface and Coatings Technology, vol. 206, pp. 1990–1997, 2011.
View at: Google Scholar
J. Cai, F. Cao, L. Chang, J. Zheng, J. Zhang, and C. Cao, “The preparation and corrosion behaviors of MAO coating on AZ91D with rare earth conversion precursor film,” Applied Surface Science, vol. 257, no. 8, pp. 3804–3811, 2011.
View at: Publisher Site | Google Scholar
Y. Gu, C.-f. Chen, S. Bandopadhyay, C. Ning, Y. Zhang, and Y. Guo, “Corrosion mechanism and model of pulsed DC microarc oxidation treated AZ31 alloy in simulated body fluid,” Applied Surface Science, vol. 258, no. 16, pp. 6116–6126, 2012.
View at: Publisher Site | Google Scholar
R. Arrabal, J. M. Mota, A. Criado, A. Pardo, M. Mohedano, and E. Matykina, “Assessment of duplex coating combining plasma electrolytic oxidation and polymer layer on AZ31 magnesium alloy,” Surface and Coatings Technology, vol. 206, no. 22, pp. 4692–4703, 2012.
View at: Publisher Site | Google Scholar
Q. Li, P. Zhu, S. Chen, B. Zhang, and K. Yang, “In vitro study on degradation of AZ31B magnesium alloy with fluoride conversion coating,” Materials Technology, vol. 32, no. 7, pp. 409–414, 2017.
View at: Publisher Site | Google Scholar
M.-H. Kang, T.-S. Jang, S. W. Kim et al., “MgF2-coated porous magnesium/alumina scaffolds with improved strength, corrosion resistance, and biological performance for biomedical applications,” Materials Science and Engineering: C, vol. 62, pp. 634–642, 2016.
View at: Publisher Site | Google Scholar
N. Li, Y. D. Li, Y. B. Wang et al., “Corrosion resistance and cytotoxicity of a MgF2 coating on biomedical Mg-1Ca alloy via vacuum evaporation deposition method,” Surface and Interface Analysis, vol. 45, no. 8, pp. 1217–1222, 2013.
View at: Publisher Site | Google Scholar
S. Li, L. Yi, X. Zhu, and T. Liu, “Ultrasonic treatment induced fluoride conversion coating without pores for high corrosion resistance of Mg alloy,” Coatings, vol. 10, no. 10, p. 996, 2020.
View at: Publisher Site | Google Scholar
M. E. Iskandar, A. Aslani, Q. Tian, and H. Liu, “Nanostructured calcium phosphate coatings on magnesium alloys: characterization and cytocompatibility with mesenchymal stem cells,” Journal of Materials Science: Materials in Medicine, vol. 26, no. 5, p. 189, 2015.
View at: Publisher Site | Google Scholar
J. Zhang, Y. Jiang, Z. Shang et al., “Biodegradable metals for bone defect repair: a systematic review and meta-analysis based on animal studies,” Bioactive Materials, vol. 6, no. 11, pp. 4027–4052, 2021.
View at: Publisher Site | Google Scholar
C. Sukotjo, T. J. Lima-Neto, J. F. Santiago Júnior, L. P. Faverani, and M. Miloro, “Is there a role for absorbable metals in surgery? A systematic review and meta-analysis of Mg/Mg alloy based implants,” Materials, vol. 13, no. 18, p. 3914, 2020.
View at: Publisher Site | Google Scholar
Y. Sun, H. Helmholz, and R. Willumeit-Römer, “Preclinical in vivo research of magnesium-based implants for fracture treatment: a systematic review of animal model selection and study design,” Journal of Magnesium and Alloys, vol. 9, no. 2, pp. 351–361, 2021.
View at: Publisher Site | Google Scholar
A. Feeley, I. Feeley, C. Ni Fhoghlú, E. Sheehan, and M. Kennedy, “Use of biomaterials in scaphoid fracture fixation, a systematic review,” Clinical Biomechanics, vol. 89, Article ID 105480, 2021.
View at: Publisher Site | Google Scholar
M. Baldini, V. Coppa, D. Falcioni, E. Senigagliesi, M. Marinelli, and A. P. Gigante, “Use of resorbable magnesium screws in children: systematic review of the literature and short-term follow-up from our series,” Journal of Children’s Orthopaedics, vol. 15, no. 3, pp. 194–203, 2021.
View at: Publisher Site | Google Scholar
N.-H. Oh, E.-Y. Kim, J. Paek et al., “Evaluation of stability of surface-treated mini-implants in diabetic rabbits,” International Journal of Dentistry, vol. 2014, Article ID 838356, 7 pages, 2014.
View at: Publisher Site | Google Scholar
S. Loretan and P. Scolozzi, “Pneumomediastinum secondary to isolated orbital floor fracture,” Journal of Craniofacial Surgery, vol. 22, no. 4, pp. 1502-1503, 2011.
View at: Publisher Site | Google Scholar
R. Cancedda, P. Giannoni, and M. Mastrogiacomo, “A tissue engineering approach to bone repair in large animal models and in clinical practice,” Biomaterials, vol. 28, no. 29, pp. 4240–4250, 2007.
View at: Publisher Site | Google Scholar
H.-S. Han, Y.-Y. Kim, Y.-C. Kim et al., “Bone formation within the vicinity of biodegradable magnesium alloy implant in a rat femur model,” Metals and Materials International, vol. 18, no. 2, pp. 243–247, 2012.
View at: Publisher Site | Google Scholar
F. Witte, V. Kaese, H. Haferkamp et al., “In vivo corrosion of four magnesium alloys and the associated bone response,” Biomaterials, vol. 26, no. 17, pp. 3557–3563, 2005.
View at: Publisher Site | Google Scholar
Y. H. Kim, S. Youn, and J. T. Kim, “Early complete bone union after condylar fracture in a child,” Journal of Craniofacial Surgery, vol. 22, no. 4, pp. 1516-1517, 2011.
View at: Publisher Site | Google Scholar
D. A. Korevaar, L. Hooft, and G. ter Riet, “Systematic reviews and meta-analyses of preclinical studies: publication bias in laboratory animal experiments,” Laboratory Animals, vol. 45, no. 4, pp. 225–230, 2011.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2022 XinYue Lu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

687

Downloads

602

Citations