Residual Stresses Introduced to Composite Structures due to the Cure Regime: Effect of Environment Temperature and Moisture

Table 3

Stresses at critical locations of the RVE after resting at room conditions, where is the First-Stress Invariant and is the stress given by Drucker-Prager failure criterion, where = 62.25 MPa and = −0.061 [10].

Location	(MPa)	(MPa)	(MPa)	(MPa)	(MPa)
P1	5.096	4.780	−5.247	4.629	61.968
P2	7.125	6.180	1.698	15.003	61.335
P3	5.074	4.750	−5.315	4.509	61.975
P4	6.334	5.223	−5.125	6.432	61.858
P5	6.790	3.566	3.378	13.734	61.412
P6	6.287	5.158	−5.220	6.225	61.870